Carbon nanocoils were prepared by the chemical vapor deposition process of the catalytic pyrolysis of acetylene at 700-800 degrees C with various catalysts. Twisting or coiling-formed carbon nanocoils with changing coiling-chirality and zigzag-formed carbon nanofibers were obtained with SUS 304, WS2, Pt-Pd, TiN, and Ni as the catalysts. Their morphologies and microstructures were examined in detail, and then the changing mechanism of the coiling-chirality was discussed. No apparent difference in the microstructure between the part of a nanocoil with changing coiling-chirality and the part of a zigzag nanofiber with changing zigzag-chirality, or between a bulk right-clockwise coil and a bulk left-clockwise coil was observed. It was supposed that changing coiling-chirality was mainly caused by the gradual or successive change in chemical composition on the thin layers present on the surface of catalyst grains during the chemical vapor deposition process.