J Mater Sci Mater Med. 2005 Feb;16(2):153-60. doi: 10.1007/s10856-005-5893-y.

Abstract

The restrained dynamic creep behaviour and mechanical properties of SmartSet GHV bone cement have been investigated at both room temperature and body temperature. It was found that the bone cement behaves significant differently at room temperature from that at body temperature. The test temperature had a strong effect on the creep performance of the bone cements with a higher creep rate observed at body temperature at each loading cycle. For both temperatures, two stages of creep were identified with a higher creep rate during early cycling followed by a steady state creep rate. The relationship between creep deformation and loading cycle can be expressed by a Hyperb 1 model. As a visco-elastic material, the sensitivity of bone cement to the temperature change was evident during mechanical testing. Compared to the mechanical strength at room temperature, a decreased value was demonstrated at body temperature. The bending modulus was very sensitive to the change in testing temperature, where a reduction of 52% was recorded. A significant reduction in compressive and bending strength, 31 and 23% were recorded respectively. The effect of temperature on bending strength was less apparent, where only 13% reduction was exhibited at body temperature compared to room temperature.

Publication types

  • Evaluation Study
  • Research Support, Non-U.S. Gov't

MeSH terms

  • Bone Cements / analysis*
  • Bone Cements / chemistry*
  • Compressive Strength
  • Elasticity
  • Hardness
  • Materials Testing
  • Molecular Weight
  • Particle Size
  • Powders
  • Temperature
  • Tensile Strength
  • Viscosity

Substances

  • Bone Cements
  • Powders