The mechanical stability of nanocrystal films is critical for applications, yet largely unexplored. Raman microprobe analysis used here to probe the nanocrystal cores of thick, fractured electrophoretically deposited films of 3.2 nm diameter CdSe nanocrystals measures approximately 2.5% in-plane tensile strain in cores of unfractured films. The crack dimensions determine the overall in-plane film strain, approximately 11.7%, and the film biaxial modulus, approximately 13.8 GPa, from which the biaxial modulus of the trioctylphosphine oxide ligand matrix is inferred, approximately 5.1 GPa.