Background: Iron and (stainless) steel are potent platelet aggregation activators, and may be involved in stent thrombosis, a serious complication after intracoronary stenting. Current platelet function tests are suboptimal, because of inappropriate agonists and/or lack of reproducibility. We tested the feasibility and reproducibility of a novel platelet function test using stainless steel as an agonist and compared it with other platelet function tests.
Materials and methods: In 111 patients with acute ST segment elevation myocardial infarction (STEMI), duplo measurements of iron (Fe)-induced platelet aggregation (FIPA) were performed after clopidogrel, acetylsalicylic acid and/or tirofiban treatment. Within 1 h, citrated blood samples drawn from the femoral sheath before primary percutaneous coronary intervention were added to 100 mg of low carbon steel and after 5 s mixing with vortex, the samples were incubated for 15 min. The ratio between the non-aggregated platelets in the agonist sample and platelets in a reference sample was calculated as the platelet aggregation inhibition.
Results: FIPA measurement was highly reproducible (correlation coefficient (R)=0.942, P<0.001 between duplo samples). FIPA correlated well with adenosine diphosphate-induced platelet aggregation (R=0.83, P<0.001) but weakly with platelet function analyser-100 bleeding time (R=0.56, P<0.001). FIPA could be measured in patients in which platelet aggregation could not be measured by platelet function analyser-100 or after adenosine diphosphate.
Conclusion: This study showed good reproducibility of a novel platelet function test using stainless steel as an agonist and showed correlation with validated platelet function tests. We found that the novel platelet function test is a suitable test for measurement of platelet aggregation inhibition in patients undergoing stenting for STEMI, even when they are taking multiple antiplatelet regimens.