Freeze-thaw Induced Biomechanical Changes in Arteries: Role of Collagen Matrix and Smooth Muscle Cells

Affiliations

Freeze-thaw Induced Biomechanical Changes in Arteries: Role of Collagen Matrix and Smooth Muscle Cells

Ramji T Venkatasubramanian et al. Ann Biomed Eng.

Abstract

Applications involving freeze-thaw, such as cryoplasty or cryopreservation can significantly alter artery biomechanics including an increase in physiological elastic modulus. Since artery biomechanics plays a significant role in hemodynamics, it is important to understand the mechanisms underlying these changes to be able to help control the biomechanical outcome post-treatments. Understanding of these mechanisms requires investigation of the freeze-thaw effect on arterial components (collagen, smooth muscle cells or SMCs), as well as the components' contribution to the overall artery biomechanics. To do this, isolated fresh swine arteries were subjected to thermal (freeze-thaw to -20 degrees C for 2 min or hyperthermia to 43 degrees C for 2 h) and osmotic (0.1-0.2 M mannitol) treatments; these treatments preferentially altered either the collagen matrix (hydration/stability) or smooth muscle cells (SMCs), respectively. Tissue dehydration, thermal stability and SMC functional changes were assessed from bulk weight measurements, analyses of the thermal denaturation profiles using Fourier transform infrared (FTIR) spectroscopy and in vitro arterial contraction/relaxation responses to norepinephrine (NE) and acetylcholine (AC), respectively. Additionally, Second Harmonic Generation (SHG) microscopy was performed on fresh and frozen-thawed arteries to directly visualize the changes in collagen matrix following freeze-thaw. Finally, the overall artery biomechanics was studied by assessing responses to uniaxial tensile testing. Freeze-thaw of arteries caused: (a) tissue dehydration (15% weight reduction), (b) increase in thermal stability (approximately 6.4 degrees C increase in denaturation onset temperature), (c) altered matrix arrangement observed using SHG and d) complete SMC destruction. While hyperthermia treatment also caused complete SMC destruction, no tissue dehydration was observed. On the other hand, while 0.2 M mannitol treatment significantly increased the thermal stability (approximately 4.8 degrees C increase in denaturation onset), 0.1 M mannitol treatment did not result in any significant change. Both 0.1 and 0.2 M treatments caused no change in SMC function. Finally, freeze-thaw (506+/-159 kPa), hyperthermia (268+/-132 kPa) and 0.2 M mannitol (304+/-125 kPa) treatments all caused significant increase in the physiological elastic modulus (Eartery) compared to control (185+/-92 kPa) with the freeze-thaw resulting in the highest modulus. These studies suggest that changes in collagen matrix arrangement due to dehydration as well as SMC destruction occurring during freeze-thaw are important mechanisms of freeze-thaw induced biomechanical changes.

Similar articles

See all similar articles

Cited by 16 PubMed Central articles

See all "Cited by" articles

Publication types

LinkOut - more resources

Feedback