Preparation of a durable superhydrophobic membrane by electrospinning poly (vinylidene fluoride) (PVDF) mixed with epoxy-siloxane modified SiO2 nanoparticles: a possible route to superhydrophobic surfaces with low water sliding angle and high water contact angle

Shuai Wang; Yapeng Li; Xiaoliang Fei; Mingda Sun; Chaoqun Zhang; Yaoxian Li; Qingbiao Yang; Xia Hong

doi:10.1016/j.jcis.2011.04.004

Preparation of a durable superhydrophobic membrane by electrospinning poly (vinylidene fluoride) (PVDF) mixed with epoxy-siloxane modified SiO2 nanoparticles: a possible route to superhydrophobic surfaces with low water sliding angle and high water contact angle

J Colloid Interface Sci. 2011 Jul 15;359(2):380-8. doi: 10.1016/j.jcis.2011.04.004. Epub 2011 Apr 14.

Authors

Shuai Wang¹, Yapeng Li, Xiaoliang Fei, Mingda Sun, Chaoqun Zhang, Yaoxian Li, Qingbiao Yang, Xia Hong

Affiliation

¹ Department of Chemistry, Jilin University, Changchun, People's Republic of China.

PMID: 21536296
DOI: 10.1016/j.jcis.2011.04.004

Abstract

A durable superhydrophobic surface with low water sliding angle (SA) and high water contact angle (CA) was obtained by electrospinning poly (vinylidene fluoride) (PVDF) which was mixed with epoxy-siloxane modified SiO(2) nanoparticles. To increase the roughness, modified SiO(2) nanoparticles were introduced into PVDF precursor solution. Then in the electrospinning process, nano-sized SiO(2) particles irregularly inlayed (it could also be regard as self-assembly) in the surface of the micro-sized PVDF mini-islands so as to form a dual-scale structure. This structure was responsible for the superhydrophobicity and self-cleaning property. In addition, epoxy-siloxane copolymer was used to modify the surface of SiO(2) nanoparticles so that the SiO(2) nanoparticles could stick to the surface of the micro-sized PVDF mini-islands. Through the underwater immersion test, the SiO(2) nanoparticles cannot be separated from PVDF easily so as to achieve the effect of durability. We chiefly explore the surface wettability and the relationship between the mass ratio of modified SiO(2) nanoparticles/PVDF and the CA, SA of electrospun mat. As the content of modified SiO(2) nanoparticles increased, the value of CA increased, ranging from 145.6° to 161.2°, and the water SA decreased to 2.17°, apparently indicating that the membrane we fabricated has a perfect effect of superhydrophobicity.