Ultrastrong Adhesion of Graphene Membranes

Affiliations

Ultrastrong Adhesion of Graphene Membranes

Steven P Koenig et al. Nat Nanotechnol.

Abstract

As mechanical structures enter the nanoscale regime, the influence of van der Waals forces increases. Graphene is attractive for nanomechanical systems because its Young's modulus and strength are both intrinsically high, but the mechanical behaviour of graphene is also strongly influenced by the van der Waals force. For example, this force clamps graphene samples to substrates, and also holds together the individual graphene sheets in multilayer samples. Here we use a pressurized blister test to directly measure the adhesion energy of graphene sheets with a silicon oxide substrate. We find an adhesion energy of 0.45±0.02 J m(-2) for monolayer graphene and 0.31±0.03 J m(-2) for samples containing two to five graphene sheets. These values are larger than the adhesion energies measured in typical micromechanical structures and are comparable to solid-liquid adhesion energies. We attribute this to the extreme flexibility of graphene, which allows it to conform to the topography of even the smoothest substrates, thus making its interaction with the substrate more liquid-like than solid-like.

Comment in

Similar articles

See all similar articles

Cited by 68 articles

See all "Cited by" articles

References

    1. Science. 2010 Apr 2;328(5974):76-80 - PubMed
    1. Science. 2008 Jul 18;321(5887):385-8 - PubMed
    1. Phys Rev Lett. 2001 Jan 1;86(1):87-90 - PubMed
    1. Nat Mater. 2005 Aug;4(8):629-34 - PubMed
    1. Nature. 2007 Mar 1;446(7131):60-3 - PubMed

Publication types

LinkOut - more resources

Feedback