Nano-composites of LiNH(2)-LiH-xMg(BH(4))(2) (0 ≤ x ≤ 2) were prepared by plasma metal reaction followed by a nucleation growth method. Highly reactive LiNH(2)-LiH hollow nanoparticles offered a favorable nucleus during a precipitation process of liquid Mg(BH(4))(2)·OEt(2). The electron microscopy results suggested that more than 90% of the obtained nano-composites were in the range 200-400 nm. Because of the short diffusion distance and ternary mixture self-catalyzing effect, this material possesses enhanced hydrogen (de)sorption attributes, including facile low-temperature kinetics, impure gases attenuation and partial reversibility. The optimal hydrogen storage properties were found at the composition of LiNH(2)-LiH-0.5Mg(BH(4))(2), which was tentatively attributed to a Li(4)(NH(2))(2)(BH(4))(2) intermediate. 5.3 wt% hydrogen desorption could be recorded at 150 °C, with the first 2.2 wt% release being reversible. This work suggests that controlled in situ hybridization combined with formula optimization can improve hydrogen storage properties.