The aim of this study was to mimic the specific structure of bone and fabricate a biomimetic nano-hydroxyapatite (HA)/chitosan (Cs)/gelatin scaffolds using combination of particle leaching and freeze drying methods eliminating mold effects. To achieve an optimum structure, scaffolds with different gelatin/Cs weight ratio were fabricated. Morphological characterization of scaffolds by scanning electron microscopy method showed highly interconnected porous structures similar to cancellous bone with mean pore size ranging from 140 to 190 μm. Nano-HA crystals were dispersed homogeneously in the polymer matrix according to the energy-dispersive X-ray spectroscopy and transmission electron microscopy images. Fourier transform infrared and X-ray diffraction results disclosed that chemical interactions were formed between nano-HA, Cs, gelatin and crystallinity of each material decreased with blending. It was found that increasing the gelatin content significantly improved water uptake, degradation rate as well as attachment, infiltration and proliferation of Saos2 cells to the scaffolds. The presented results confirm that the designed biomimetic nano-HA /Cs/gelatin scaffolds can be used as promising substitutes for bone tissue engineering.
Keywords: bone tissue engineering; chitosan/gelatin; freeze drying; nano-hydroxyapatite; particle leaching.
© 2014 Wiley Periodicals, Inc.