Background: The purpose of this study was to determine the effect of three chewing gums and paraffin on the remineralization and the hardness of demineralized enamel.
Materials and methods: A total of 12 subjects wore intraoral palatal appliances with two demineralized bovine enamel slabs. The study consisted of four experimental periods each lasting 21-days, during which subjects were assigned to one of three gum-chewing regimens: gum containing sorbitol, xylitol and a mixture of sorbitol and xylitol and with paraffin as control. The appliances were worn during gum-chewing for 20 min and then retained for 20 min 4 times/day. The slabs were subjected to energy dispersive X-ray spectroscopy analysis and surface microhardness measurements before in setting into the appliance and after the experimental period. The data were subjected to analysis of variance for repeated measures. A P < 0.05 was considered statistically significant.
Results: Mineral analysis revealed no significant difference between the baseline and after chewing periods for all groups (P > 0.05). No significant difference was found among the groups either for the baseline measurements or after chewing periods (P > 0.05). All groups showed higher microhardness values after the chewing periods than the baseline except for the Vivident Xylit group (P < 0.05).
Conclusion: The chewing of gum had no effect on the Ca/P ratio of demineralized enamel surfaces. The hardening of the demineralized enamel surfaces may vary according to the type of chewing gum.
Keywords: Chewing gum; enamel; energy dispersive X-ray spectroscopy; microhardness.