We present an approach for the synthesis of ternary copper indium sulfide (CIS) and quaternary copper indium zinc sulfide (CIZS) nanocrystals (NCs) by means of partial cation exchange with In(3+) and Zn(2+). The approach consists of a sequential three-step synthesis: first, binary Cu2S NCs were synthesized, followed by the homogeneous incorporation of In(3+) by an in situ partial cation-exchange reaction, leading to CIS NCs. In the last step, a second partial exchange was performed where Zn(2+) partially replaced the Cu(+) and In(3+) cations at the surface, creating a ZnS-rich shell with the preservation of the size and shape. By careful tuning reaction parameters (growth and exchange times as well as the initial Cu(+):In(3+):Zn(2+) ratios), control over both the size and composition was achieved. This led to a broad tuning of photoluminescence of the final CIZS NCs, ranging from 880 to 1030 nm without altering the NCs size. Cytotoxicity tests confirmed the biocompatibility of the synthesized CIZS NCs, which opens up opportunities for their application as near-infrared fluorescent markers in the biomedical field.
Keywords: Stokes shift engineering; alloys; cation exchange; copper indium sulfide; copper indium zinc sulfide; copper sulfide; cyclic voltammetry; nanocrystals; photoluminescence.