Development of pseudocapacitor electrode materials with high comprehensive electrochemical performance, such as high capacitance, superior reversibility, excellent stability, and good rate capability at the high mass loading level, still is a tremendous challenge. To our knowledge, few works could successfully achieve the above comprehensive electrochemical performance simultaneously. Here we design and synthesize one interwoven three-dimensional (3D) architecture of cobalt oxide nanobrush-graphene@Ni(x)Co(2x)(OH)(6x) (CNG@NCH) electrode with high comprehensive electrochemical performance: high specific capacitance (2550 F g(-1) and 5.1 F cm(-2)), good rate capability (82.98% capacitance retention at 20 A g(-1) vs 1 A g(-1)), superior reversibility, and cycling stability (92.70% capacitance retention after 5000 cycles at 20 A g(-1)), which successfully overcomes the tremendous challenge for pseudocapacitor electrode materials. The asymmetric supercapacitor of CNG@NCH//reduced-graphene-oxide-film exhibits good rate capability (74.85% capacitance retention at 10 A g(-1) vs 0.5 A g(-1)) and high energy density (78.75 Wh kg(-1) at a power density of 473 W kg(-1)). The design of this interwoven 3D frame architecture can offer a new and appropriate idea for obtaining high comprehensive performance electrode materials in the energy storage field.
Keywords: Three-dimensional frame architecture; cobalt oxide nanobrush-graphene@nickle-cobalt hydroxides; comprehensive performance; pseudocapacitor materials; tremendous challenge.