Here, we report solid solution of p- and n-type organic semiconductors as a new type of p-n blend for solution-processed ambipolar organic thin film transistors (OTFTs). This study compares the solid-solution films of silylethynylated tetraazapentacene 1 (acceptor) and silylethynylated pentacene 2 (donor) with the microphase-separated films of 1 and 3, a heptagon-embedded analogue of 2. It is found that the solid solutions of (1)x(2)1-x function as ambipolar semiconductors, whose hole and electron mobilities are tunable by varying the ratio of 1 and 2 in the solid solution. The OTFTs of (1)0.5(2)0.5 exhibit relatively balanced hole and electron mobilities comparable to the highest values as reported for ambipolar OTFTs of stoichiometric donor-acceptor cocrystals and microphase-separated p-n bulk heterojunctions. The solid solution of (1)0.5(2)0.5 and the microphase-separated blend of 1:3 (0.5:0.5) in OTFTs exhibit different responses to light in terms of absorption and photoeffect of OTFTs because the donor and acceptor are mixed at molecular level with π-π stacking in the solid solution.
Keywords: ambipolar; microphase separation; organic semiconductors; organic thin film transistors; solid solution.