Aqueous Solution-Deposited Gallium Oxide Dielectric for Low-Temperature, Low-Operating-Voltage Indium Oxide Thin-Film Transistors: A Facile Route to Green Oxide Electronics

Affiliations

Aqueous Solution-Deposited Gallium Oxide Dielectric for Low-Temperature, Low-Operating-Voltage Indium Oxide Thin-Film Transistors: A Facile Route to Green Oxide Electronics

Wangying Xu et al. ACS Appl Mater Interfaces.

Abstract

We reported a novel aqueous route to fabricate Ga2O3 dielectric at low temperature. The formation and properties of Ga2O3 were investigated by a wide range of characterization techniques, revealing that Ga2O3 films could effectively block leakage current even after annealing in air at 200 °C. Furthermore, all aqueous solution-processed In2O3/Ga2O3 TFTs fabricated at 200 and 250 °C showed mobilities of 1.0 and 4.1 cm2 V(-1) s(-1), on/off current ratio of ∼10(5), low operating voltages of 4 V, and negligible hysteresis. Our study represents a significant step toward the development of low-cost, low-temperature, and large-area green oxide electronics.

Keywords: aqueous route; gallium oxide dielectric; green oxide electronics; indium oxide; low-temperature; oxide thin-film transistors.

Similar articles

See all similar articles

Publication types

LinkOut - more resources

Feedback