A solid/mist reaction method is developed to produce well-crystallized light harvester layers without pinhole defects for perovskite solar cells. The reaction based on mist precursor can be facilely operated with low process temperature. And it can effectively control the volume of CH3NH3I solution and the reaction temperature, which affect the quality of perovskite harvester layers and the performance of perovskite solar cells remarkably. Under optimized condition, the efficiencies of devices reach 16.2% with the average efficiency of 14.9%. The solid/mist reaction is also used to fabricate planar junction solar cells and a PCE of 14.9% is obtained.
Keywords: interface reaction; low-temperature fabrication; mist; morphology-control; perovskite formation process; solar cells.