A dense and homogenous flat wide-bandgap (1.75 eV) CH3NH3PbI2.1Br0.9 perovskite film was prepared via a facile halide exchange route. The planar-heterojunction solar cell shows an optimal power conversion efficiency of 12.67% with negligible current hysteresis due to the film's large grains and vertically oriented grain boundaries.