A simple approach was developed for rapid preparation of polymeric monolithic columns in UV-transparent fused-silica capillaries via photoinitiated thiol-acrylate polymerization of pentaerythritol diacrylate monostearate (PEDAS) and trimethylolpropane tris(3-mercaptopropionate) (TPTM) within 10min, in which the acrylate homopolymerized and copolymerized with the thiol simultaneously. The morphology, permeability and chromatographic performance of the resulting poly(PEDAS-co-TPTM) monoliths were studied. It could be observed from SEM that the morphology of poly(PEDAS-co-TPTM) monolith was rather different from that of poly(PEDAS) monolith, which was fabricated via photo-induced free radical polymerization using PEDAS as the sole monomer. Compared with poly(PEDAS) monolith, poly(PEDAS-co-TPTM) monolith possessed better permeability when they were fabricated under the same preparation conditions. By adjusting the composition of porogenic solvents, poly(PEDAS-co-TPTM) monolith exhibited lower plate heights (15.7-17.7μm) than poly(PEDAS) monolith (19.1-37.9μm) in μLC. In addition, 66 unique peptides were positively identified on poly(PEDAS-co-TPTM) monolith when tryptic digest of four proteins was separated by μLC-MS/MS, demonstrating its potential in proteome analysis.
Keywords: 2,2-Dimethoxy-2-phenylacetophenone; Pentaerythritol diacrylate monostearate; Photoinitiated; Polymeric monoliths; Thiol-acrylate polymerization; Trimethylolpropane tris(3-mercaptopropionate).
Copyright © 2016 Elsevier B.V. All rights reserved.