Large increasing production volumes of automotive shredder residue (ASR) and its hazardous content have raised concerns worldwide. ASR has a desirable calorific value, making its pyrolysis a possible, environmentally friendly and economically viable solution. The present work focuses on the pyrolysis of ASR at temperatures between 950 and 1550°C. Despite the high temperatures, the energy consumption can be minimized as the decomposition of ASR can be completed within a short time. In this study, the composition of ASR was investigated. ASR was found to contain about 3% Ti and plastics of high calorific value such as polypropylene, polyethylene, polycarbonate and polyurethane. Based on thermogravimetric analysis (TGA) of ASR, the non-isothermal degradation kinetic parameters were determined using Coats-Redfern's and Freeman and Carroll methods. The evolved gas analysis indicated that the CH4 was consumed by the reduction of some oxides in ASR. The reduction reactions and the presence of Ti, silicates, C and N in ASR at 1550°C favor the formation of specific ceramics such as TiN and SiC. The presence of nano-ceramics along with a highly-crystalline graphitic carbon in the pyrolysis residues obtained at 1550°C was confirmed by scanning electron microscopy (SEM), X-ray powder diffraction (XRD) and Raman imaging microscope (RIM) analyses.
Keywords: Automotive shredder residue; High temperature transformation; Nano-ceramics; Titanium nitride; Waste as resources; Waste pyrolysis.
Copyright © 2016 Elsevier Ltd. All rights reserved.