With our recently developed deformation device, the in situ tensile tests of single crystal molybdenum nanowires with various size and aspect ratio were conducted inside a transmission electron microscope (TEM). We report an unusual ambient temperature (close to room temperature) super-plastic elongation above 127% on single crystal body-centred cubic (bcc) molybdenum nanowires with an optimized aspect ratio and size. A novel dislocation "bubble-like-effect" was uncovered for leading to the homogeneous, large and super-plastic elongation strain in the bcc Mo nanowires. The dislocation bubble-like-effect refers to the process of dislocation nucleation and annihilation, which likes the nucleation and annihilation process of the water bubbles. A significant plastic deformation dependence on the sample's aspect ratio and size was revealed. The atomic scale TEM observations also demonstrated that a single crystal to poly-crystal transition and a bcc to face-centred cubic phase transformation took place, which assisted the plastic deformation of Mo in small scale.