Relevant aspects in the surface properties in titanium dental implants for the cellular viability

Abstract

Roughness and topographical features are the most relevant of the surface properties for a dental implant for its osseointegration. For that reason, we studied the four surfaces more used in titanium dental implants: machined, sandblasted, acid etching and sandblasted plus acid etching. The roughness and wettability (contact angle and surface free energy) was studied by means 3D-interferometric microscope and sessile drop method. Normal human gingival fibroblasts (HGF) were obtained from small oral mucosa biopsies and were used for cell cultures. To analyze cell integrity, we first quantified the total amount of DNA and LDH released from dead cells to the culture medium. Then, LIVE/DEAD assay was used as a combined method assessing cell integrity and metabolism. All experiments were carried out on each cell type cultured on each Ti material for 24h, 48h and 72h. To evaluate the in vivo cell adhesion capability of each Ti surface, the four types of discs were grafted subcutaneously in 5 Wistar rats. Sandblasted surfaces were significantly rougher than acid etching and machined. Wettability and surface free energy decrease when the roughness increases in sand blasted samples. This fact favors the protein adsorption. The DNA released by cells cultured on the four Ti surfaces did not differ from that of positive control cells (p>0.05). The number of cells per area was significantly lower (p<0.05) in the sand-blasted surface than in the machined and surface for both cell types (7±2 cells for HGF and 10±5 cells for SAOS-2). The surface of the machined-type discs grafted in vivo had a very small area occupied by cells and/or connective tissue (3.5%), whereas 36.6% of the sandblasted plus acid etching surface, 75.9% of sandblasted discs and 59.6% of acid etching discs was covered with cells and connective tissue. Cells cultured on rougher surfaces tended to exhibit attributes of more differentiated osteoblasts than cells cultured on smoother surfaces. These surface properties justify that the sandblasted implants is able to significantly increase bone contact and bone growth with very good osseointegration results in vivo.

Keywords: Bone index contact; Cellular behavior; Roughness treatments; Surface free energy; Titanium; Wettability.