Purpose: The purpose of this study was to compare the removal torques of a chemically modified SLActive implant and a blasted, laser-treated (BLT) implant, which were soaked in saline for 2 weeks after their surface modifications. The removal torques of the two implants were measured 4 weeks after their implantation into the bone defect area in rabbit tibias with concentrated growth factor (CGF) application.
Materials and methods: To make artificial bone defects in the cortical layers of both tibias, an 8-mm diameter trephine bur was used. Then, prepared CGF was applied to the bony defect of the left tibia, and the bony defect of the right tibia was left unfilled. Four weeks later, the surgical sites of 16 rabbits were re-exposed. For 8 rabbits, the SLActive implants (Straumann, Switzerland) were inserted in the left tibia, and the BLT implants (CSM implant, Daegu, Korea) were inserted in the right tibia. For other rabbits, the BLT implants were inserted in the left tibia, and the SLActive implants were inserted in the right. Four weeks afger the insertion, torque removal was measured from 4 rabbits exterminated via CO2 inhalation.
Results: No significant difference was observed between removal torques of the BLT implant and the SLActive implant (P>.05).
Conclusion: It was found that BLT surface modification exhibited excellent osseointegration. In addition, CGF application did not affect the insertion and removal torque of the implants.
Keywords: Concentrated growth factor (CGF); Laser-treated implant; Removal torque; SLActive.