A one-dimensional porous carbon-supported Ni/Mo2C dual catalyst for efficient water splitting

Zi-You Yu; Yu Duan; Min-Rui Gao; Chao-Chao Lang; Ya-Rong Zheng; Shu-Hong Yu

doi:10.1039/c6sc03356c

A one-dimensional porous carbon-supported Ni/Mo₂C dual catalyst for efficient water splitting

Chem Sci. 2017 Feb 1;8(2):968-973. doi: 10.1039/c6sc03356c. Epub 2016 Sep 30.

Authors

Zi-You Yu¹, Yu Duan¹, Min-Rui Gao¹, Chao-Chao Lang¹, Ya-Rong Zheng¹, Shu-Hong Yu¹

Affiliation

¹ Division of Nanomaterials and Chemistry , Hefei National Laboratory for Physical Sciences at Microscale , Collaborative Innovation Center of Suzhou Nano Science and Technology , CAS Center for Excellence in Nanoscience , Hefei Science Center of CAS , Department of Chemistry , University of Science and Technology of China , Hefei , Anhui 230026 , P. R. China . Email: shyu@ustc.edu.cn ; ; Tel: +86-551-63603040.

Abstract

The development of active, stable and low-cost electrocatalysts towards both the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) for overall water splitting remains a big challenge. Herein, we report a new porous carbon-supported Ni/Mo₂C (Ni/Mo₂C-PC) composite catalyst derived by thermal treatment of nickel molybdate nanorods coated with polydopamine, which efficiently and robustly catalyses the HER and OER with striking kinetic metrics in alkaline electrolyte. The catalyst affords low onset potentials of -60 mV for the HER and 270 mV for the OER, as well as small overpotentials of 179 mV for the HER and 368 mV for the OER at a current density of 10 mA cm^-2. These results compare favorably to Mo₂C-PC, Ni-PC, and most other documented Ni- and Mo-based catalysts. The high activity of Ni/Mo₂C-PC is likely due to electron transfer from Ni to Mo₂C, leading to a higher Ni valence and a lower Mo valence in the Ni/Mo₂C-PC catalyst, as these are HER and OER active species and thus account for the enhanced activity. Remarkably, our home-made alkaline electrolyser, assembled with Ni/Mo₂C-PC as a bifunctional catalyst, can enable a water-splitting current density of 10 mA cm^-2 to be achieved at a low cell voltage of 1.66 V.