Adverse local tissue reactions to corrosion products can lead to total hip arthroplasty failure. Although this problem has been well known for more than 25 years, it has seemingly increased in frequency over the recent years. The occurrence of corrosion is multifactorial-depending on implant, patient, and surgeon factors. As of now, there is no "one-size-fits-all" solution to prevent corrosion in total hip arthroplasty devices. Thus, it is imperative to fully understand the exact mechanisms of modular junction corrosion to prevent premature implant failure. This review highlights a few key concepts that need to be explored to minimize the impact of corrosion. The key concepts include (1) the prevention of micromotion, (2) the role of implant alloy metallurgy in the corrosion process, (3) the in vivo generation of a corrosive environment, and (4) potential unanticipated problems.
Keywords: adverse tissue reactions; corrosion; fretting; modular junction; taper; total hip arthroplasty.