Objective and background: The correct selections of the cementing agent, the endodontic post material and placement protocol are critical to provide an increased longevity of the teeth that went through endodontic treatment. The irradiation with diode laser before post cementation, can promote an antimicrobial effect. However, there is a lack of information about the effect of 830 nm diode laser on the post bond strength. This study analyzed the effect of dentin root canal irradiation with high-intensity diode laser, at 830 nm, operating in continuous or pulsed mode, on the retention of metal or fiber posts, cemented with self-etching resinous composite (Panavia F) and zinc phosphate cement (ZnPO4).
Materials and methods: Human roots were irradiated with diode laser (continuous and pulsed mode). The fiber posts were luted with Panavia F and the metal posts with Panavia F or ZnPO4 cement. Specimens were sectioned into three sections (cervical, middle, and apical). The bond strength was measured by a push-out mechanical analysis. For the statistical analysis, a three-way ANOVA test was applied following a Tukey's pairwise comparison with a significance level of p = 0.05.
Results: The irradiated groups presented higher bond strength compared with nonirradiated group (p < 0.05), and the cervical and middle thirds presented higher on bond strength than the apical. The association of metal post and Panavia F presented higher bond strength when irradiated on continuous mode (p < 0.05). Fiber post and Panavia F presented higher bond strength associated to pulsed mode. The mode seems not to make a significant difference.
Conclusions: These results corroborate the importance of the post bond to dentin and root canal debris removal to increase the tooth longevity. It was shown that the dentin to post bond strength were enhanced by the diode laser irradiation either on continuous or pulsed modes.
Keywords: bond strength; diode laser; fiber post; metal post; push-out test.