Background:: This in vitro study aimed to evaluate the amount of polymerizing light passing through hybrid ceramic specimens in different shades and thicknesses.
Methods:: Rectangular-shaped feldspathic ceramic computer aided design and computer aided manufacturing (CAD-CAM) blocks and translucent and high translucent polymer infiltrated hybrid ceramic CAD-CAM blocks in four different shades (1M1, 1M2, 2M2, and 3M2) were sectioned in four different thicknesses (0.8, 1.5, 2, and 3 mm), and a total of 48 groups ( n = 10) were obtained. Feldspathic ceramic specimens served as the control group. The light transmission of each ceramic specimen was measured three times by using a light-emitting diode and a radiometer. Data were statistically analyzed by using univariate analysis of variance (ANOVA) followed by one-way ANOVA, Tukey honest significant difference, and Tamhane T2 tests (α = 0.05).
Results:: Translucent polymer infiltrated hybrid ceramic specimens exhibited significantly ( p < 0.001) lower light transmission values than high translucent polymer infiltrated hybrid ceramic and feldspathic ceramic specimens, whereas feldspathic ceramic specimens exhibited significantly ( p < 0.001) higher light transmission than translucent and high translucent polymer infiltrated hybrid ceramic specimens. The amount of light transmission significantly ( p < 0.05) decreased when the shade value decreased and the thickness increased.
Conclusions:: Polymer infiltrated hybrid ceramic specimens showed lower light transmission values than feldspathic ceramic specimens, and the amount of light transmission was affected by the ceramic shade and thickness.
Keywords: Polymer infiltrated ceramics; light transmission; resin cement polymerization.