Vanadium hexacyanoferrate (VHCF) with an open-framework crystal structure is a promising cathode material for rechargeable aqueous metal-ion batteries owing to its high electrochemical performance and easy synthesis. In this paper, vanadium hexacyanoferrate cathodes were first used for constructing rechargeable aqueous sodium-ion batteries (VHCF/WO3) and tested in the new-type electrolyte (NaP-4.6) consisting of a polyethylene glycol (PEG)/H2O/NaClO4 electrolyte with a low H+ concentration (molar ratio of [H2O]/[Na+] is 4.6), which has high stability at a high current density as high as 1000 mA g-1 with a capacity retention of 90.3% after 2000 cycles at high coulombic efficiency (above 97.8%). To understand their outstanding performance, the proton-assisted sodium-ion storage mechanism and interphase chemistry of VHCF are investigated by solid-state NMR (ssNMR) technology. It is suggested that the H+ storage reaction is accompanied by the redox of vanadium atoms and Na+ intercalation is accompanied by the redox of iron atoms. It is also observed that the complex of polyethylene glycol (PEG) with Na+ (PEG-Na+) exists on the VHCF surface, which facilitates the stability of VHCF and promotes the alkali-ion transfer at a high current density. The results of the ssNMR study offer new insights into the intercalation chemistry of Prussian blue analogues with open-framework-structured compounds, which can greatly broaden our horizons for battery research.
Keywords: Aqueous rechargeable sodium-ion battery; Solid electrolyte interphase; Solid-state NMR; Vanadium hexacyanoferrate.