This paper presents results of experimental investigation into dielectric properties of silicon oxide lignin (SiO2-L) particles dispersed with various mass fractions in ethylene glycol (EG). Measurements were conducted at a controlled temperature, which was changed from 298.15 to 333.15 K with an accuracy of 0.5 and 0.2 K for dielectric properties and direct current (DC) electrical conductivity, respectively. Dielectric properties were measured with a broadband dielectric spectroscopy device in a frequency range from 0.1 to 1 MHz, while DC conductivity was investigated using a conductivity meter MultiLine 3410 working with LR925/01 conductivity probe. Obtained results indicate that addition of even a small amount of SiO2-L nanoparticles to ethylene glycol cause a significant increase in permittivity and alternating current (AC) conductivity as well as DC conductivity, while relaxation time decrease. Additionally, both measurement methods of electrical conductivity are in good agreement.
Keywords: electrical properties; lignin; nanofluids; nanoparticles; silica; silicon oxide.