Ceramic oxide electrolytes are outstanding due to their excellent thermostability, wide electrochemical stable windows, superior Li-ion conductivity, and high elastic modulus compared to other electrolytes. To achieve high energy density, all-solid-state batteries require thin solid-state electrolytes that are dozens of micrometers thick due to the high density of ceramic electrolytes. Perovskite-type Li0.34 La0.56 TiO3 (LLTO) freestanding ceramic electrolyte film with a thickness of 25 µm is prepared by tape-casting. Compared to a thick electrolyte (>200 µm) obtained by cold-pressing, the total Li ionic conductivity of this LLTO film improves from 9.6 × 10-6 to 2.0 × 10-5 S cm-1 . In addition, the LLTO film with a thickness of 25 µm exhibits a flexural strength of 264 MPa. An all-solid-state Li-metal battery assembled with a 41 µm thick LLTO exhibits an initial discharge capacity of 145 mAh g-1 and a high capacity retention ratio of 86.2% after 50 cycles. Reducing the thickness of oxide ceramic electrolytes is crucial to reduce the resistance of electrolytes and improve the energy density of Li-metal batteries.
Keywords: Li-metal batteries; oxide ceramics; solid-state electrolytes; tape casting; ultrathin films.
© 2019 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.