Ultrathin core-shell V3 S4 @C nanosheets assembled into hierarchical nanotubes (V3 S4 @C NS-HNTs) are synthesized by a self-template strategy and evaluated as general anodes for alkali-ion batteries. Structural/physicochemical characterizations and DFT calculations bring insights into the intrinsic relationship between crystal structures and electrochemical mechanisms of the V3 S4 @C NS-HNTs electrode. The V3 S4 @C NS-HNTs are endowed with strong structural rigidness owing to the layered VS2 subunits and interlayer occupied V atoms, and efficient alkali-ion adsorption/diffusion thanks to the electroactive V3 S4 -C interfaces. The resulting V3 S4 @C NS-HNTs anode exhibit distinct alkali-ion-dependent charge storage mechanisms and exceptional long-durability cyclic performance in storage of K+ , benefiting from synergistic contributions of pseudocapacitive and reversible intercalation/de-intercalation behaviors superior to those of the conversion-reaction-based Li+ -/Na+ -storage counterparts.
Keywords: V3S4@C nanosheets; alkali-ion batteries; density functional calculations; hierarchical nanotubes.
© 2019 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.