In this study, the wear behavior of glazed zirconia was investigated to the antagonist with human enamel after simulated mastication. Twenty Y-TZP specimens were divided into 4 groups: untreated zirconia (Z), glazed zirconia with IPS e.max Ceram (GZE), glazed zirconia with VITA AKZENT® Plus (GZV), and glazed zirconia with glass (GZG). Glazing glass was mainly composed of SiO₂, B₂O₃, Al₂O₃, Na₂O and K₂O (nearly 91 wt%). The surface roughness of the specimens was evaluated using roughness profiler. The maxillary premolar teeth were selected as the antagonist. The wear of human enamel against human enamel was used as a control. Five-disc specimens per group were subjected to chewing stimulation CS-4 (SD Mechatronic GmbH, Germany) for 240,000 cycles against human enamel. The wear loss of antagonistic teeth was calculated using a three-dimensional profiling system and the volume loss of the tooth was scanned using a 3D scanner. 3D data obtained before and after testing were overlapped using 3D software (Dentacian Software, EZplant, Korea). The wear loss of glazed zirconia GZE, GZV and GZG groups showed significantly lower than that of human enamel. Whereas, the zirconia (Z) group exhibits significantly lower volume loss than glazed zirconia and enamel. These results show that the wear of the glazing glass is comparable to other commercial glazing materials. Glazing materials are both more susceptible to wear the antagonist relative to zirconia.