Structural Insight into the Abnormal Capacity of a Co-Substituted Tunnel-Type Na0.44MnO2 Cathode for Sodium-Ion Batteries

Wentao Zhong; Qianhui Huang; Fenghua Zheng; Qiang Deng; Qichang Pan; Yanzhen Liu; Youpeng Li; Yijuan Li; Junhua Hu; Chenghao Yang; Meilin Liu

doi:10.1021/acsami.0c13278

Structural Insight into the Abnormal Capacity of a Co-Substituted Tunnel-Type Na_0.44MnO₂ Cathode for Sodium-Ion Batteries

ACS Appl Mater Interfaces. 2020 Oct 21;12(42):47548-47555. doi: 10.1021/acsami.0c13278. Epub 2020 Oct 8.

Authors

Affiliations

¹ Guangzhou Key Laboratory for Surface Chemistry of Energy Materials, New Energy Research Institute, School of Environment and Energy, South China University of Technology, Guangzhou 510006, China.
² School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001, China.
³ School of Materials Science & Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332-0245, United States.

PMID: 32990426
DOI: 10.1021/acsami.0c13278

Abstract

Tunnel-type (T-type) Na_0.44MnO₂ (NMO) is a promising cathode material for sodium-ion batteries (SIBs) owing to its high rate performance and cycling stability compared to manganese-based layered oxides. However, the low specific capacity still restricts its practical applications. Herein, a Co-doped T-type NMO is synthesized through a facile solid-state reaction method and utilized as a cathode material for SIBs. A T-type Na_0.44Mn_0.9925Co_0.0075O₂ (NMO-3) electrode can deliver a high reversible capacity of 138 mAh g^-1 at 0.1C, a superior rate capability (133, 130, 121, 106, and 93 mAh g^-1 at 0.5, 1, 2, 5, and 10C, respectively), and excellent cycling stability (85.2% at 10C after 500 cycles). The substitution of Co³⁺ by Mn³⁺ leads to the enlargement of small and S-shaped tunnel spaces, which facilitates the insertion/deinsertion of Na⁺ into/from NMO-3 and greatly enhances its rate capability and cycling stability. Moreover, the reduced energy barriers for Na⁺ diffusion in small tunnels make the inactive Na⁺ easier to be deintercalated, which should be responsible for its high specific capacity that exceeds the theoretical capacity of T-type NMO.

Keywords: Co-substitution; DFT calculation; cathode materials; sodium-ion batteries; tunnel-type Na0.44MnO2.