This study compared titanium (Ti), palladium (Pd), platinum (Pt), and gold (Au) ion release following induced accelerated tribocorrosion from three Au alloy abutment groups coupled with Ti implants over time; investigated contacting surface structural changes; and explored the effect of Au plating. Three abutment groups, G (n = 8, GoldAdapt, Nobel Biocare), N (n = 8, cast UCLA, Biomet3i), and P (n = 8, cast UCLA, Biomet3i, Au plated), coupled with implants (Nobel Biocare), immersed in 1% lactic acid, were cyclically loaded. Ions released (ppb) at T1, T2, and T3, simulating 3, 5, and 12 months of function, respectively, were quantified by inductively coupled plasma mass spectrometry (ICP-MS) and compared. Surface degradation and fretted particle composition after T3 were evaluated with scanning electron microscopy and energy-dispersive X-ray spectroscopy (SEM/EDX). ICP-MS data were nonparametric, expressed as medians and interquartile ranges. SEM/EDX showed pitting, crevice corrosion, and fretted particles on the components. Released ion concentrations in all groups across time significantly decreased for Pd (P < .001, median range: 1.70-0.09), Pt (P = .021, 0.55-0.00), and Au (P < .001, 1.01-0.00) and increased for Ti (P = .018, 2.49-5.84). Total Ti release was greater than other ions combined for G (P = .012, 9.86-2.30) and N (P < .001, 13.59-5.70) but not for P (P = .141, 8.21-3.53). Total Ti release did not differ between groups (P = .36) but was less variable across group P. On average, total ion release was 13.77 ppb (interquartile range 8.91-26.03 ppb) across the 12-month simulation. Tribocorrosion of Ti implants coupled with Au abutments in a simulated environment was evidenced by fretted particles, pitting, and crevice corrosion of the coupling surfaces and release of ions. More Ti was released compared with Pd, Pt, and Au and continued to increase with time. Abutment composition influenced ion release. Au-plated abutments appeared to subdue variation in and minimize high-concentration spikes of titanium.
Keywords: corrosion; dental implants; electrochemical deposition; gold plating; ion release; peri-implant bone loss; titanium.