Unimolecular amphiphilic nanoreactors with a poly(4-vinyl-N-methylpyridinium iodide) (P4VPMe+ I- ) polycationic outer shell and two different architectures (core-cross-linked micelles, CCM, and nanogels, NG), with narrow size distributions around 130-150 nm in diameter, were synthesized by RAFT polymerization from an R0 -4VPMe+ I- 140 -b-S50 -SC(S)SPr macroRAFT agent by either chain extension with a long (300 monomer units) hydrophobic polystyrene-based block followed by cross-linking with diethylene glycol dimethacrylate (DEGDMA) for the CCM particles, or by simultaneous chain extension and cross-linking for the NG particles. A core-anchored triphenylphosphine (TPP) ligand functionality was introduced by using 4-diphenylphosphinostyrene (DPPS) as a comonomer (5-20 % mol mol-1 ) in the chain extension (for CCM) or chain extension/cross-linking (for NG) step. The products were directly obtained as stable colloidal dispersions in water (latexes). After loading with [RhCl(COD)]2 to yield [RhCl(COD)(TPP@CCM)] or [RhCl(COD)(TPP@NG)], respectively, the polymers were used as polymeric nanoreactors in Rh-catalyzed aqueous biphasic hydrogenation of the model substrates styrene and 1-octene, either neat (for styrene) or in an organic solvent (toluene or 1-nonanol). All hydrogenations were rapid (TOF up to 300 h-1 ) at 25 °C and 20 bar of H2 pressure, the biphasic mixture rapidly decanted at the end of the reaction (<2 min), the Rh loss was negligible (<0.1 ppm in the recovered organic phase), and the catalyst phase could be recycled 10 times without significant loss of catalytic activity.
Keywords: nanostructures; polycations; polymers; rhodium; self-assembly; surfactants.
© 2020 Wiley-VCH GmbH.