Multinary layered 2D nanomaterials can exhibit distinct physicochemical properties and innovative applications as compared to binary 2D nanomaterials due to their unique crystal structures. However, it still remains a challenge for the high-yield preparation of high-quality multinary 2D nanosheets. Here, the high-yield and large-scale production of two quaternary metal thiophosphate nanosheets are reported, i.e., Ni3 Cr2 P2 S9 and Ni3 Cr2 P2 Se9 , via the liquid exfoliation of their layered bulk crystals. The exfoliated single-crystalline Ni3 Cr2 P2 S9 nanosheets, with a lateral size ranging from a few hundred nanometers to a few micrometers and thickness of 1.4 ± 0.2 nm, can be easily used to prepare flexible thin films via a simple vacuum filtration process. As a proof-of-concept application, the fabricated thin film is used as a supercapacitor electrode with good specific capacitance. These high-yield, large-scale, solution-processable quaternary metal thiophosphate nanosheets could also be promising in other applications like biosensors, cancer therapies, and flexible electronics.
Keywords: Ni 3Cr 2P 2S 9; Ni 3Cr 2P 2Se 9; nanosheets; quaternary metal thiophosphates; supercapacitors.
© 2021 Wiley-VCH GmbH.