Pharyngoesophageal defects can cause exposure to various bacterial flora and severe inflammation. We fabricated a biodegradable polycaprolactone (PCL) patch composed of both thin film and three-dimensional (3D) printed lattice, and then investigated the efficacy of pharyngoesophageal reconstruction by using 3D printed antibiotic-releasing PCL patches that inhibited early inflammation by sustained tetracycline (TCN) release from both thin PCL films and printed rods implanted in esophageal partial defects. PCL was 3D printed in lattice form on a presolution casted PCL thin film at ∼100 μm resolution. TCN was loaded onto the PCL-printed patches by 3D printing a mixture of TCN and PCL particles melted at 100°C. TCN exhibited sustained release in vitro for over 1 month. After loading TCN, the patches showed decreased tensile strength and Young's modulus, and less than 20% TCN was slowly released from the 2.5% TCN-loaded PCL patches over 150 days. Cytotoxicity tests of extract solutions from patch samples demonstrated excellent in vitro cell compatibility. Antibiotic-releasing PCL patches were then transplanted into partial esophageal defects in rats. Microcomputed tomography analysis revealed no leak of orally injected contrast agent in the entire esophagus. Tissue remodeling was examined through histological responses of M1 and M2 macrophages. In particular, the 1% and 3% TCN patch groups exhibited significant muscle layer regeneration by desmin immunostaining. Further histological and immunofluorescence analyses revealed that the 1% and 3% TCN patch groups exhibited the best esophageal regeneration according to reepithelialization, neovascularization, and elastin texture around the implanted sites. Our antibiotic-releasing patch successfully consolidates the regenerative potential of esophageal muscle and mucosa and the antibacterial activity of TCN for 3D esophageal reconstruction. Impact statement Anastomosis site leakage and necrosis after pharyngoesophageal transplantation inevitably causes mortality because the mediastinum and neck compartments become contaminated. Herein, we present antibiotic-releasing pharyngoesophageal patch that prevents saliva leakage and has an antimicrobial effect. We have demonstrated antibiotic release profile and mechanical properties for esophageal transplantation. Upon esophageal transplantation of antibiotic-releasing polycaprolactone patches, antimicrobial effects and muscle regeneration around the graft sites were clearly identified in the group containing 1% and 3% of tetracycline. The esophageal graft led to the remarkable recovery throughout reepithelialization, neovascularization, and elastin texture of around the implanted sites. We believe that current system is capable of various applications that require antibacterial in vivo.
Keywords: antibiotic-releasing patch; antimicrobial activity; esophageal patch; tissue regeneration.