In the present work, a hybrid magnetic field assisted powder mixed electrical discharge machining had been carried out on the Aluminum-Silicon Carbide (Al-SiC) metal matrix composite. The aim of the study was to obtain higher surface finish, and enhanced material removal rate. The dielectric mediums employed were plain EDM oil, SiCp mixed and graphite powder mixed EDM oil for flushing through the tube electrode. The magnetic field intensity, discharge current, T-on/off duration and type of dielectric were the control variables used for present investigation. From the results, it was observed that the machining variables for instance, discharge current, T-on/off duration and type of dielectric conditions remarkably affected the material removal rate, micro-hardness and surface roughness of the machined composite material. The MRR augmented considerably with an increase in the magnetic field intensity along with peak current. Subsequently, the composite with lesser vol.% of SiC particulates witnessed sharp rise in MRR in maximum magnetic field environment (0.66T). In addition, quality of the machined surface improved significantly in graphite powder mixed dielectric flushing condition with intermediate external magnetic field environment. Besides, an enhancement of micro-hardness was quantified as compared to base material due to the transfer of the material (SiCp) during powder mixed ED machining.
Keywords: Taguchi; electrical discharge machining; material removal rate; metal matrix composite; micro-hardness; surface roughness.