A novel three-dimensional graphene-like networks material (3D-GLN) exhibiting the hierarchical porous structure was fabricated with a large-scale preparation method by employing an ion exchange resin as a carbon precursor. 3D-GLN was first studied as the effective microwave absorbing material. As indicated from the results of the electromagnetic parameter tests, and the minimum reflection loss (RL) of the 3D-GLN reached -34.75 dB at the frequency of 11.7 GHz. To enhance the absorption performance of the nonmagnetic 3D-GLN, the magnetic Fe3O4 nanoparticles were loaded on the surface of the 3D-GLN by using the hydrothermal method to develop the 3D-GLN/Fe3O4 hybrid. The hybrid exhibited the prominent absorbing properties. Under the matching thickness of 3.0 mm, the minimum RL value of hybrid reached -46.8 dB at 11.8 GHz. In addition, under the thickness range of 2.0-5.5 mm, the effective absorption bandwidth (RL < 10 dB) was 13.0 GHz, which covered part of the C-band and the entire X-band, as well as the entire Ku-band. The significant microwave absorption could be attributed to the special 3D network structure exhibited by the hybrid and the synergistic effect exerted by the graphene and the Fe3O4 nanoparticles. As revealed from the results, the 3D-GLN/Fe3O4 hybrid could be a novel microwave absorber with promising applications.
Keywords: Fe3O4; graphene-like; hybrid; impedance matching; microwave absorption; networks.