Engineering Leaf-Like UiO-66-SO3H Membranes for Selective Transport of Cations

Tingting Xu; Muhammad Aamir Shehzad; Xin Wang; Bin Wu; Liang Ge; Tongwen Xu

doi:10.1007/s40820-020-0386-6

Engineering Leaf-Like UiO-66-SO₃H Membranes for Selective Transport of Cations

Nanomicro Lett. 2020 Feb 17;12(1):51. doi: 10.1007/s40820-020-0386-6.

Authors

Tingting Xu¹, Muhammad Aamir Shehzad¹, Xin Wang¹, Bin Wu², Liang Ge³, Tongwen Xu⁴

Affiliations

¹ CAS Key Laboratory of Soft Matter Chemistry, iCHEM (Collaborative Innovation Center of Chemistry for Energy Materials), Department of Applied Chemistry, School of Chemistry and Materials Science, University of Science and Technology of China, Hefei, 230026, People's Republic of China.
² School of Chemistry and Chemical Engineering, Key Laboratory of Environment-Friendly Polymeric Materials of Anhui Province, Anhui University, Hefei, 230601, People's Republic of China.
³ CAS Key Laboratory of Soft Matter Chemistry, iCHEM (Collaborative Innovation Center of Chemistry for Energy Materials), Department of Applied Chemistry, School of Chemistry and Materials Science, University of Science and Technology of China, Hefei, 230026, People's Republic of China. geliang@ustc.edu.cn.
⁴ CAS Key Laboratory of Soft Matter Chemistry, iCHEM (Collaborative Innovation Center of Chemistry for Energy Materials), Department of Applied Chemistry, School of Chemistry and Materials Science, University of Science and Technology of China, Hefei, 230026, People's Republic of China. twxu@ustc.edu.cn.

Abstract

Metal-organic frameworks (MOFs) with angstrom-sized pores are promising functional nanomaterials for the fabrication of cation permselective membranes (MOF-CPMs). However, only a few research reports show successful preparation of the MOF-CPMs with good cation separation performance due to several inherent problems in MOFs, such as arduous self-assembly, poor water resistance, and tedious fabrication strategies. Besides, low cation permeation flux due to the absence of the cation permeation assisting functionalities in MOFs is another big issue, which limits their widespread use in membrane technology. Therefore, it is necessary to fabricate functional MOF-CPMs using simplistic strategies to improve cation permeation. In this context, we report a facile in situ smart growth strategy to successfully produce ultrathin (< 600 nm) and leaf-like UiO-66-SO₃H membranes at the surface of anodic alumina oxide. The physicochemical characterizations confirm that sulfonated angstrom-sized ion transport channels exist in the as-prepared UiO-66-SO₃H membranes, which accelerate the cation permeation (~ 3× faster than non-functionalized UiO-66 membrane) and achieve a high ion selectivity (Na⁺/Mg²⁺ > 140). The outstanding cation separation performance validates the importance of introducing sulfonic acid groups in MOF-CPMs.

Keywords: In situ smart growth; Ion separation; Metal–organic frameworks; UiO-66-SO3H membrane.