Objective: The effect of different photoinitiators on mechanical properties of experimental composites was evaluated.
Materials and methods: Resin composites were formulated by using a blend of bisphenol A-glycidyl and triethylene glycol (50/50 wt%) dimethacrylate monomers, and 65 wt% of barium aluminium silicate and silica filler particles. Photoinitiators used were 0.2% camphorquinone (CQ) and 0.8% co-initiator (DMAEMA); 0.2% phenyl-propanedione and 0.8% DMAEMA; 0.1% CQ + 0.1% phenyl propanedione and 0.8% DMAEMA; 0.42% mono(acyl)phosphine oxide (MAPO); and 0.5% bis(acyl)phosphine oxide (BAPO). Specimens (n = 10) were light cured by using a multiple-emission peak light-emitting diode for 20 seconds at 1,200 mW/cm2 of irradiance and Knoop hardness and plasticization, depth of cure, flexural strength, and elastic modulus were evaluated. Data were statiscally analyzed at significance level of α = 5%.
Results: Experimental composites containing MAPO and BAPO photoinitiators showed the highest values of flexural strength, elastic modulus, top surface hardness, and lower hardness reduction caused by alcohol compared with CQ. Composites containing CQ and PPD showed similar results, except for depth of cure and hardness of bottom surface.
Conclusion: BAPO and MAPO showed higher flexural strength, elastic modulus, hardness on top surface, and lower polymer plasticization to CQ.
The Author(s). This is an open access article published by Thieme under the terms of the Creative Commons Attribution License, permitting unrestricted use, distribution, and reproduction so long as the original work is properly cited. (https://creativecommons.org/licenses/by/4.0/).