(1) Background: This study investigated the miscibility of carbon-based fillers within industrial scale polymers for the preparation of superior quality polymer composites. It focuses on finding the light distribution in gamma irradiated ultra-high molecular weight polyethylene (UHMWPE). (2) Methods: The Kubleka-Munk model (KMM) was used to extract the optical properties, i.e., absorption coefficients (μa) and scattering coefficients (μs). Samples amounting to 30 kGy and 100 kGy of irradiated (in the open air) UHMWPE from 630 nm to 800 nm were used for this purpose. Moreover, theoretical validation of experimental results was performed while using extracted optical properties as inputs for the Monte Carlo model of light transport (MCML) code. (3) Conclusions: The investigations revealed that there was a significant decrease in absorption and scattering coefficient (μa & μs) values with irradiation, and 30 kGy irradiated samples suffered more compared to 100 kGy irradiated samples. Furthermore, the simulation of light transport for 800 nm showed an increase in penetration depth for UHMWPE after gamma irradiation. The decrease in dimensionless transport albedo μs(μa+μs) from 0.95 to 0.93 was considered responsible for this increase in photon absorption per unit area with irradiation. The report results are of particular importance when considering the light radiation (from 600 nm to 899 nm) for polyethylene modification and/or stabilization via enhancing the polyethylene chain mobility.
Keywords: Kubleka–Munk model; Monte Carlo simulation; UHMWPE; chain mobility; gamma irradiations; photon distribution.