Synthetic hydroxyapatite-based solution is a bioinspired material that may present anti-adhesive properties, restraining the dental biofilm formation without causing adverse effects. This in situ study aims to evaluate the effects of three different hydroxyapatite (HAP) watery solutions as a mouthwash against biofilm adhesion on different dental material surfaces under oral conditions. Hence, four volunteers carried maxillary splints containing enamel, titanium, ceramics, and polymethyl-methacrylate resin (PMMA) samples. Three HAP watery solutions (5%) were prepared with HAP particles presenting different shapes and sizes (HAP I, HAP II, HAP III). During 24 h, the volunteers rinsed two times with one of the following selected tested solution: HAP I, HAP II, HAP III, water, or chlorhexidine 0.2% (CHX). The first rinse was performed 3 min after pellicle formation; the second rinse occurred after a 12 h interval. The surface analysis was performed by scanning electron microscopy (SEM), fluorescence microscopy (FM), and transmission electron microscopy (TEM). Statistical and microscopic analysis showed that most samples treated with any HAP solution revealed reduced biofilm coverage presenting comparable results to CHX treated samples, however without altering the microorganisms' viability. In conclusion, the results of this investigation showed that a pure hydroxyapatite-based mouthrinse could be a promising bioinspired adjunct solution for biofilm management.
Keywords: biomaterials; hydroxyapatite; nanomaterials; oral biofilm.