Poly(N-vinylcaprolactam) (PNVCL) is a suitable alternative for biomedical applications due to its biocompatibility, biodegradability, non-toxicity, and showing phase transition at the human body temperature range. The purpose of this study was to synthesize a high molecular weight PNVCL-PVAc thermo-responsive copolymer with broad mass distribution suitable for electrospun nanofiber fabrication. The chemical structure of the synthesized materials was detected by FTIR and 1HNMR spectroscopies. N-Vinyl caprolactam/vinyl acetate copolymers (159,680 molecular weight (g/mol) and 2.51 PDI) were synthesized by radical polymerization. The phase transition temperature of N-vinyl caprolactam/vinyl acetate copolymer was determined by conducting a contact angle test at various temperatures (25, 26, 28, and 30 [Formula: see text]). The biocompatibility of the nanofibers was also evaluated, and both qualitative and quantitative results showed that the growth and proliferation of 929L mouse fibroblast cells increased to 80% within 48 h. These results revealed that the synthesized nanofibers were biocompatible and not cytotoxic. The results confirmed that the synthesized copolymers have good characteristics for biomedical applications.
Keywords: Biomedical applications; LCST; PNVCL-b-PVAc; Phase transition temperature; Radical copolymerization; Thermo-responsive copolymer.
© 2021. The Author(s), under exclusive licence to Islamic Azad University.