A series of lignin-based epoxy resins (LEPs) were prepared by the reaction of epichlorohydrin with lignin oligomers derived from partial reductive depolymerization of lignin. To overcome the high viscosity and brittleness defects in practical applications, the LEPs were blended with renewable epoxied cardanol glycidyl ether (ECGE) and then cured with methyltetrahydrophthalic anhydride (MeTHPA) to form high-performance epoxy thermosets. The effects of degree of lignin depolymerization, chemical composition of lignin oligomers and dosage of ECGE on thermal and mechanical properties of the cured products were investigated. The LEP/MeTHPA thermosets exhibited good thermal and mechanical properties. Especially, by separating monomer-rich fractions from lignin oligomers, the thermal and mechanical properties of the cured product were improved obviously. Notably, the incorporation of ECGE also possessed a positive effect on reinforcing and toughening the cured products. With 20 wt% ECGE loadings, the tensile, flexural and impact strength of the cured product reached the maximum value of 77 MPa, 115 MPa and 14 kJ/m2, respectively, which were equivalent to the commercial bisphenol A epoxy resins thermosets. These findings indicated that the novel bio-based epoxy resins from lignin oligomers and cardanol could be utilized as renewable alternatives for BPA epoxy resins.
Keywords: Alkali lignin; Cardanol; Epoxy resin; Property; Reductive depolymerization.
Copyright © 2021. Published by Elsevier B.V.