Aging of 3D Printed Polymers under Sterilizing UV-C Radiation

Polymers (Basel). 2021 Dec 20;13(24):4467. doi: 10.3390/polym13244467.

Abstract

In the context of the COVID-19 pandemic, shortwave ultraviolet radiation with wavelengths between 200 nm and 280 nm (UV-C) is seeing increased usage in the sterilization of medical equipment, appliances, and spaces due to its antimicrobial effect. During the first weeks of the pandemic, healthcare facilities experienced a shortage of personal protective equipment. This led to hospital technicians, private companies, and even members of the public to resort to 3D printing in order to produce fast, on-demand resources. This paper analyzes the effect of accelerated aging through prolonged exposure to UV-C on mechanical properties of parts 3D printed by material extrusion (MEX) from common polymers, such as polylactic acid (PLA) and polyethylene terephthalate-glycol (PETG). Samples 3D printed from these materials went through a 24-h UV-C exposure aging cycle and were then tested versus a control group for changes in mechanical properties. Both tensile and compressive strength were determined, as well as changes in material creep properties. Prolonged UV-C exposure reduced the mechanical properties of PLA by 6-8% and of PETG by over 30%. These findings are of practical importance for those interested in producing functional MEX parts intended to be sterilized using UV-C. Scanning electron microscopy (SEM) was performed in order to assess any changes in material structure.

Keywords: 3D-printing; PETG; PLA; UV-C; accelerated aging; ultraviolet.