In this work, a copper coating is developed on a carbon steel substrate by exploiting the superwetting properties of liquid copper. We characterize the surface morphology, chemical composition, roughness, wettability, ability to release a copper ion from surfaces, and antibacterial efficacy (against Escherichia coli and Staphylococcus aureus). The coating shows a dense microstructure and good adhesion, with thicknesses of approximately 20-40 µm. X-ray diffraction (XRD) analysis reveals that the coated surface structure is composed of Cu, Cu2O, and CuO. The surface roughness and contact angle measurements suggest that the copper coating is rougher and more hydrophobic than the substrate. Inductively coupled plasma atomic emission spectroscopy (ICP-AES) measurements reveal a dissolution of copper ions in chloride-containing environments. The antibacterial test shows that the copper coating achieves a 99.99% reduction of E. coli and S. aureus. This study suggests that the characteristics of the copper-coated surface, including the chemical composition, high surface roughness, good wettability, and ability for copper ion release, may result in surfaces with antibacterial properties.
Keywords: antibacterial properties; coating; copper; fine crevice structure; super-spread wetting properties.