In this article, highly porous and transparent silicon oxycarbide (SiOC) gels are synthesized from Bis(Triethoxysilyl) methane (BTEM). The gels are synthesized by the sol-gel technique followed by both ambient pressure and supercritical drying. Then, the portion of wet gels have been pyrolyzed in a hydrogen atmosphere at 800 and 1100 °C. The FT-IR spectroscopy analysis and nitrogen sorption results indicate the successful synthesis of Si-O-Si bonds and the formation of mesopores. From a hysteresis loop, the SiOC ceramics showed the H1 type characteristic with well-defined cylindrical pore channels for the aerogel and the H2 type for the ambigel samples, indicating that the pores are distorted due to the capillary stress. The produced gels are mesoporous materials having high surface areas with a maximum of 1140 m2/g and pore volume of 2.522 cm3/g obtained from BTEM aerogels. The pyrolysis of BTEM aerogels at 800 °C results in the production of a bulk and transparent sample with a slightly pale white color, while BTEM xerogels are totally transparent and colorless at the same temperature. At 1100 °C, all the aerogels become opaque brown, confirming the formation of free carbon and crystalline silicon.
Keywords: SiOC ceramics; aerogel; sol-gel; supercritical CO2 drying and porous materials.