Although the dry ice method used to synthesize turbostratic carbon/graphene is little known and used, it has significant advantages over others, such as the following: it is low cost, simple, and a large quantity of material can be obtained using some inorganic and highly available acids (which can be reused). Despite the above advantages, the main reason for its incipient development is the resulting presence of magnesium oxide in the final product. In the present work, three different treatments were tested to remove this remnant using some acid chemical leaching processes, including hydrochloric acid, aqua regia, and piranha solution. Based on the experimental evidence, it was determined that using aqua regia and combining the leaching process with mechanical milling was the most efficient way of removing such a remnant, the residue being only 0.9 wt.%. This value is low compared to that obtained with the other acid leaching solutions and purification processes (2.8-29.6 wt.%). A mandatory high-energy mechanical milling stage was necessary during this treatment to expose and dissolve the highly insoluble oxide without secondary chemical reactions on the turbostratic carbon. High-energy mechanical milling is an effective route to exfoliate graphite, which allows the magnesium oxide to be more susceptible to acid treatment. A yield of turbostratic carbon/graphene of 1 wt.% was obtained from the metallic Mg. The obtained surface area was 504.8 m2g-1; this high value resulting from the intense exfoliation can potentiate the use of this material for a wide variety of applications.
Keywords: dry ice; graphene; magnesium oxide; mechanical milling; turbostratic carbon.