The creation and application of PET nanofibrils for PP composite reinforcement were studied. PET nanofibrils were fibrillated within a PP matrix using a spunbond process and then injection molded to test for the end-use properties. The nanofibril reinforcement helped to provide higher tensile and flexural performance in solid (unfoamed) injection molded parts. With foam injection molding, the nanofibrils also helped to improve and refine the microcellular morphology, which led to improved performance. Easily and effectively increasing the strength of a polymeric composite is a goal for many research endeavors. By creating nanoscale fibrils within the matrix itself, effective bonding and dispersion have already been achieved, overcoming the common pitfalls of fiber reinforcement. As blends of PP and PET are drawn in a spunbond system, the PET domains are stretched into nanoscale fibrils. By adapting the spunbonded blends for use in injection molding, both solid and foamed nanocomposites are created. The injection molded nanocomposites achieved increased in both tensile and flexural strength. The solid and foamed tensile strength increased by 50 and 100%, respectively. In addition, both the solid and foamed flexural strength increased by 100%. These increases in strength are attributed to effective PET nanofibril reinforcement.
Keywords: fiber reinforced thermoplastics; fibrillated nanofibers; foam injection molding; nano composites.