The aim of this systematic review was to provide an overview of the technical and clinical outcomes of conventional, speed sintering and high-speed sintering protocols of zirconia in the dental field. Data on precision, mechanical and optical parameters were evaluated and related to the clinical performance of zirconia ceramic. The PICOS search strategy was applied using MEDLINE to search for in vitro and in vivo studies using MeSH Terms by two reviewers. Of 66 potentially relevant studies, 5 full text articles were selected and 10 were further retrieved through a manual search. All 15 studies included in the systematic review were in vitro studies. Mechanical, precision and optical properties (marginal and internal fit, fracture strength and modulus, wear, translucency and opalescence, aging resistance/hydrothermal aging) were evaluated regarding 3-, 4- and 5-YTZP zirconia material and conventional, high- and high-speed sintering protocols. Mechanical and precision results were similar or better when speed or high-speed sintering methods were used for 3-, 4- and 5-YTZP zirconia. Translucency is usually reduced when 3 Y-TZP is used with speed sintering methods. All types of zirconia using the sintering procedures performed mechanically better compared to lithium disilicate glass ceramics but glass ceramics showed better results regarding translucency.
Keywords: aesthetics; all-ceramic; clinical outcome; cost efficacy; dental; dental materials; firing; mechanical; post-processing; pre-processing; prosthetic dentistry; sintering; speed sintering; systematic review; technical; time efficacy; zirconia; zirconium dioxide.