How to effectively reduce the damage of frequent accidental explosions and explosion attacks to existing walls is an important concern of the blast resistance field. In the present study, the influence of the foamed concrete (density 820 kg/m3, water-cement ratio 0.4) coating thickness on the blast resistance of a 120 mm RC (reinforced concrete) wall was studied through blast experiments, numerical simulations, and shock wave theory. Results show that the influences of foamed concrete on the blast resistance of RC walls are jointly decided by the stress drop caused by impedance effect and exponential attenuation and the stress rise caused by high-speed impact compression. The coating thickness mainly affects the foam concrete's fragmentation degree and stress attenuation. A lower critical coating thickness exists in foamed concrete-coated RC walls. The blast resistance of the RC wall will decrease when the coating thickness is less than that value. The lower critical coating thickness is related to the intensity of blast load and the energy absorption capacity of foamed concrete, and it can be predicted by monitoring the explosive stress and energy incident to the RC wall.
Keywords: RC wall; blast resistance; coating thickness; energy absorption; foamed concrete.